Review about corrosion of superheaters tubes in biomass plants

Authors

  • C. Berlanga-Labari Departamento de Ingeniería Mecánica, Energética y de Materiales. Universidad Pública de Navarra.
  • J. Fernández-Carrasquilla Departamento de Ingeniería Mecánica, Energética y de Materiales. Universidad Pública de Navarra.

DOI:

https://doi.org/10.3989/revmetalm.2006.v42.i4.29

Keywords:

High temperature corrosion, Deposits corrosion, Gaseous corrosion, Biomass, Superheater

Abstract


The design of new biomass-fired power plants with increased steam temperature raises concerns of high-temperature corrosion. The high potassium and chlorine contents in many biomasses, specially in wheat straw, are potentially harmful elements with regard to corrosion. Chlorine may cause accelerated corrosion resulting in increased oxidation, metal wastage, internal attack, void formations, and loose non-adherent scales. The most severe corrosion problems in biomass-fired systems are expected to occur due to Cl-rich deposits formed on superheater tubes. In the first part of this revision the corrosion mechanism proposed are described in function of the conditions and compounds involved. The second part is focused on the behaviour of the materials tested so far in the boiler and in the laboratory. First the traditional commercial alloys are studied and secondly the new alloys and the coatings

Downloads

Download data is not yet available.

References

[1] L.L. Baxter, T.R. Miles, B.M. Jenkins Y D. Dayton, The behaviour of inorganic material in a biomass-fired power boilers-field and laboratory experiences, vol. II of Alkali deposits found in a biomass power plants, National Renewable Energy Laboratory (Eds.), Colorado, EE.UU., 1996.

[2] B. Sander, Biomass Bioener. 10 (1997) 122- 177.

[3] L.L. Baxter Y H.P. Nielsen, Proc. American Chemical Society Fuel Division, Bringham, EE.UU., 1997, pp. 154.

[4] H.P. Nielsen, Tesis Doctoral, Departamento de Ingeniería Química, Universidad Técnica de Dinamarca, 1998.

[5] H.P. Michelsen, O.H. Larsen Y F.J. Frandsen, Fuel Process. Technol. (1998) 54-59.

[6] P.L. Daniel Y R.A. Rapp, Advances in Corrosion Science and Technology, Vol 5., Plenum Press (Eds), Nueva York, EE. UU., 1976.

[7] K.N. Strafford, P.K. Datta Y G. Foster, Mat. Sci. Eng. A 120 (1989) 61-68. doi:10.1016/0921-5093(89)90719-3

[8] A.S. Kim Y M.J. Mcnallan, Corrosion 46 (1990) 746-755.

[9] S.Y. Lee Y M.J. Mcnallan, Corrosion 47 (1991) 868-874.

[10] V.A.C. Haanappel, N.W.J. Haanappel Y T. Frandsen, Corrosion 48 (1992) 812-821.

[11] H. Chu, P.K. Datta, J.S. Gray Y K.N. Strafford, Corros. Sci. 35 (1993) 1091-1098. doi:10.1016/0010-938X(93)90328-E

[12] H.J. Grabke, M. Spiegel Y E. Reese, Corros. Sci. 37 (1995) 1.023-1.043.

[13] Y.N. Chang Y F.I. Wei, J. Mater. Sci. 26 (1991) 3.693-3.698.

[14] Y. Ihara, H. Oghame, K. Sakiyama Y K. Hashimoto, Corros. Sci. 23 (1983) 167-181. doi:10.1016/0010-938X(83)90114-2

[15] J.N. Harb Y E.E. Smith, Prog. Energ. Combust. 16 (1990) 169-190. doi:10.1016/0360-1285(90)90048-8

[16] M.K. Hossain Y R.J. Saunders, Oxid. Met. 12 (1978) 1-22. doi:10.1007/BF00609972

[17] P.A. Alexander, The Mechanics of Corrosion by Fuel Impurities, Londres, U.K., 1963, pp. 571.

[18] R.C. John, High Temperature Corrosion in Energy Systems, AIME (Eds), EE.UU., 1984, pp 501.

[19] C.J. Wang, C.C. Tsaur Y J.C. Rock, Mater. Chem. Phys. 89 (2005) 445-453. doi:10.1016/j.matchemphys.2004.10.002

[20] C.J. Wang, J.W. Lee Y J.G. Duh, J. Mater. Sci. 38 (2003) 3.619-3.628.

[21] C.J. Wang, Y.C. Chang Y Y.H. Su, Oxid. Met. 59 (2003) 115-133. doi:10.1023/A:1023022100300

[22] C.J. Wang Y C.C. Li, Oxid. Met. 61 (2004) 485- 505. doi:10.1023/B:OXID.0000032335.40917.4f

[23] C.J. Wang Y T.T. He, Oxid. Met. 58 (2002) 234- 242.

[24] C.J. Wang Y J.S. Lin, Mater. Chem. Phys. 76 (2002) 123-129. doi:10.1016/S0254-0584(01)00527-2

[25] C.J. Wang Y Y.C. Chang, Mater. Chem. Phys. 76 (2002) 151-161. doi:10.1016/S0254-0584(01)00515-6

[26] P. Hancock, Mater. Sci. Tech. 88 (1987) 303- 311.

[27] Y. Shinata, F. Takahashi Y K. Hashiura, Mater Sci. Eng. 87 (1987) 399-405. doi:10.1016/0025-5416(87)90404-6

[28] H. Fujikawa Y N. Maruyama, Mater. Sci. Eng. A 120 (1989) 301-306. doi:10.1016/0921-5093(89)90754-5

[29] N. Hiramatsu, Y. Uematsu, T. Tanaka Y M. Kinugasa, Mater Sci. Eng. A (120) 301- 306.

[30] L.D. Paul Y P.L. Daniel, Mater. Perform. 27 (1989) 22-25.

[31] K. Gotthjaelp, P. Bronsted, P. Jansen, J. Markussen, M. Montgomery y E. Maahan, High Temperature Corrosion in Biomass Incineration Plants, Project nº 1323/95-0008, Universidad Técnica de Dinamarca, 1996.

[32] A.J.B. Cutler, W.D. Halstead, J.W. Laxton y C.G. Stevens, J. Eng. Power 93 (1971) 307.

[33] P.D. Miller, H.H. Krause, J. Zupan y W. Boyd, Corrosion 28 (1972) 272

[34] D.A. Vaughan, H.H. Krause y W.D. Boyd, Proc. International Conference of Ash Deposits and Corrosion from impurities from combustion gases, Henniker, New Hampshier, EE.UU., 1997, pp. 473.

[35] K. Salmeneja, K. Makela, M. Hupa y R. Backman, J. Int. Energy 69 (1996) 155-162.

[36] M. Spiegel, H.P. Grabke, Incineration Industrial and Municipal Waste, R.W. Bryers (Eds), Nueva York, EE.UU.,1978, pp 758.

[37] P. Kofstad, High Temperature Corrosion, Elsevier Applied Science (Eds), New York, EE.UU., 1988.

[38] N. Otsuka, T. Kudo y Y. Saito, High Temperature Corrosion of Advanced Materials and Protective Coatings, Elsevier (Eds), Amsterdam, Holanda,1992.

[39] A. Karlsson, P.J. Moller y V. Johansen, Corros. Sci. 30 (1990) 153-158. doi:10.1016/0010-938X(90)90069-H

[40] Y. Schinata, Oxid. Met. 27 (1987) 315-332. doi:10.1007/BF00659274

[41] Y. Schinata y Y. Nishi, Oxid. Met. 26 (1986) 201-216. doi:10.1007/BF00659184

[42] W.T. Reid, External Corrosion and Deposits, Ed Elsevier, Nueva York, EE.UU., 1971.

[43] A.J.B. Cutler y E. Raask, Corros. Sci. 21 (1981) 789-800. doi:10.1016/0010-938X(81)90089-5

[44] R.A. Raap, Corrosion 42 (1986) 568.

[45] Guidelines for methods of testing for research in high temperature corrosion, European Federation of Corrosion Publications (Eds), nº 14, 1995.

[46] S. Sroda Y S. Tuurna, Mater. Corros. 57 (2006) 244-251. doi:10.1002/maco.200503931

[47] S. Sroda Y M. Makipaa Y S.C. CHA, Mater. Corros. 57 (2006) 176-181. doi:10.1002/maco.200503906

[48] S. Sroda, D. Baxter Y M. Arponen, Mater. Corros. 56 (2005) 791-795. doi:10.1002/maco.200503880

[49] S Sroda, S Tuurna, Y K. Penttila, Mater. Sci. Forum 461-464 (2004) 981-988.

[50] M. Makipaa, D. Baxter Y S. Sroda, Mater. Sci. Forum 461-464 (2004) 989-997.

[51] V. Higuera-Hidalgo, F.J. Belzunce-Varela Y J. Riba-Lopez, Rev. Metal. Madrid 41 (2005) 204-211.

[52] F. Almeraya, A. Martinez-Villafane Y C. Gaona, Rev. Metal. Madrid 34 (1998) 11-17

[53] E. Otero, A. Pardo, M.C. Merino, M.V. Utrilla, M.D. Lopez Y J.L. Del Peso, Oxid. Met. 51 (1999) 507-525. doi:10.1023/A:1018895312069

[54] E. Otero, A.Pardo, F.J. Perez, M.V. Utrilla Y T.Levi, Oxid. Met. 49 (1998) 467-484. doi:10.1023/A:1018851029023

[55] E. Otero, A. Pardo, F.J. Perez, M.V. Utrilla, T. Levi, M.L. Casado Y M.C. Merino, Mater. Sci. Forum 251-254 (1997) 519-526.

[56] N. Henriksen, O.H. Larsen Y R. Blum, Proc. VGB Conference in Corrosion in Power Plants, 1995, pp. 1-10.

[57] N. Henriksen, O.H. Larsen Y R. Blum, Proc. 9 th European Bioenergy Conference, Loughborough, U.K.,1996.

[58] F.J. Frandsen, K. Dam-Johanesen Y H.P. Michelsen, Fuel Process. Technol. 54 (1998) 95-108. doi:10.1016/S0378-3820(97)00062-3

[59] M. Montgomery Y A. Karlsson, Mater. Corros. 50 (1999) 579-584. doi:10.1002/(SICI)1521-4176(199910)50:10<579::AID-MACO579>3.0.CO;2-M

[60] M. Montgomery, A. Karlsson Y O.H. Larsen, Mater Corros. 53 (2002) 121-131. doi:10.1002/1521-4176(200202)53:2<121::AID-MACO121>3.0.CO;2-R

[61] M. Montgomery, A. Karlsson Y O.H. Larsen, Mater. Corros. 53 (2002) 185-194. doi:10.1002/1521-4176(200203)53:3<185::AID-MACO185>3.0.CO;2-K

[62] M. Montgomery, A. Karlsson Y O.H. Larsen, Proc. VDI Conference, Alemania, 2002.

[63] C. Berlanga-Labari Y J. Fernández-Carrasquilla, Proc. Eurocorr 05, European Federation of Corrosion (Eds), Lisboa, Portugal, 2005.

[64] I. Gutiérrez-Urrutia, I. Gallego, M.L. Nó Y J.M. San Juan, Rev. Metal. Madrid 37 (2001) 98-102.

[65] P.A. Jensen, F.J. Fradsen, K. Dam-Johanesen, J. Hansen, N. Henriksen Y J. Jansen, Enero. Fuel. 18 (2004) 378-384. doi:10.1021/ef030097l

[66] P. Andersson, M. Norell Y R. Gautheron, Mater. Sci. Forum 461-464 (2004) 1.015- 1.022.

[67] S. C. Cha Y M. Spiegel, Mater. Corros. 56 (2006) 159-164.

[68] S.C. Cha Y M. Spiegel, Corros. Eng. Sci. Tech. 40 (2005) 249-254. doi:10.1179/174327805X66317

[69] S.C. Cha Y M. Spiegel, Corrosion 61 (2005) 743-750

[70] A. Zahs, H.P. Grabke Y M. Spiegel, Mater. Corros. 50 (1999) 561-578.

[71] Y. Uematsu, N. Hiramatsu, T. Tanaka Y M. Kinugasa, Mater. Sci. Eng. A 120-121 (1989) 319-328. doi:10.1016/0921-5093(89)90757-0

[72] Y. LI, Y.S. Niu Y W.T. Wu, Mater. Sci. Eng A 345 (2003) 64-69. doi:10.1016/S0921-5093(02)00386-6

[73] Y. Shinata, Oxid. Met. 27 (1987) 201-209. doi:10.1007/BF00659274

[74] Y.S. LI, M. Spiegel Y M. Sanchez-Pasten, Mater. Sci. Forum 461-464 (2004) 1.047-1.054.

[75] F. Wang Y Y. Shu, Oxid. Met. 59 (2003) 201-214. doi:10.1023/A:1023083309041

[76] Y. S.Liu Y M. Spiegel, Oxid. Met. 61 (2004) 303-308. doi:10.1023/B:OXID.0000025337.64394.bf

[77] C.J. Wang Y Y.C. Chang, Mater. Chem. Phys. 76 (2002) 151-161. doi:10.1016/S0254-0584(01)00515-6

[78] F.H. Stott Y G.C. Wood, Mater. Sci. Tech. 4 (1988) 1072-1078.

[79] F.A. Lang Y Z.M. Yu, Intermetallics 11 (2003) 135-141. doi:10.1016/S0966-9795(02)00190-5

[80] G. Han Y W.D. Cho, Oxid. Met. 58 (2002) 391-413. doi:10.1023/A:1020167023654

[81] Y. Kawahara, Corros. Sci. 44 (2002) 223-245. doi:10.1016/S0010-938X(01)00058-0

[82] Y.S. LI, M. Spiegel Y S. Shimada, Mater. Chem. Phys. 93 (2005) 217-223. doi:10.1016/j.matchemphys.2005.03.015

[83] E.P. Lathan, D.B. Meadowcroft Y L. Pinder, Mater. Sci. Tech. 5 (1989) 813-815.

[84] U. Brill Y G.K. Grossmann, Proc. Corrosion 2001, Paper nº170, NACE (Eds.), Houston, EE.UU.

[85] J. Stringer, Surf. Coat. Tech. 108-109 (1998) 1-9. doi:10.1016/S0257-8972(98)00642-2

[86] V. Rohr, M. Schutze, E. Fortuna, A. Milewska Y F.J. Perez, Mater. Corros. 56 (2006) 874-881. doi:10.1002/maco.200503918

[87] V. Rohr, A. Donchev, M. Schutze, A. Milewska Y F.J. Perez, Corr Eng. Sci. Tech. 40 (2005) 226-232 doi:10.1179/174327805X66272

[88] E.J. Morgan-Warren, Weld Met. Fab. 60 (1992) 21-22.

[89] M.S. Breenan Y R.C. Gassmann, Proc. Corrosion 2000, Paper nº 235, NACE (Eds), Orlando, EE.UU.

[90] V. Higuera-Hidalgo, F.J. Belzunce-Varela, S. Poveda-Martínez Rev. Metal. Madrid 40 (2004) 347-351.

[91] C.J. Wang Y C.C. LI, Surf. Coat. Tech. 177-178 (2004) 37-43. doi:10.1016/j.surfcoat.2003.06.004

[92] C.J. Wang, J.W. Lee Y T.H. Twu, Surf. Coat. Tech. 163-164 (2003) 37-44. doi:10.1016/S0257-8972(02)00588-1

[93] Y.S. LI, M. Spiegel Y S. Shimada, Mater. Lett. 58 () 3.787-3.791.

[94] M.A. Uusitalo, P.M.J. Vuoristo Y T.A. Mantyla, Mater. Sci. Eng. A 346 (2003) 168-177. doi:10.1016/S0921-5093(02)00537-3

[95] M.A. Uusitalo, P.M.J. Vuoristo Y T.A. Mantyla, Surf. Coat. Tech. 161 (2002) 275- 285. doi:10.1016/S0257-8972(02)00472-3

[96] P. Pérez, F.J. Pérez, C. Gómez Y P. Adeva, Rev. Metal. Madrid Vol. Extr. (2005) 255-259.

[97] F.J. Pérez, J.A. Trillero, M.A. Hierro, A. Milewska, M.C. Carptintero Y F.J. Bolivar, Mater Sci Forum 461-464 (2004) 313-319.

[98] D.A. Skobir M. Spiegel, A Milewska, F.J. Pérez, V. Rohr Y M. Schutze, Proc. Eurrocorr. 2005, European Federation of Corrosion (Eds), Lisboa, Portugal, 2005.

[99] N.J. Simms, S.R.J. Saunders, S. Osgerby Y J.E. Oakey, Mater. High Temp. 20 (2003) 137- 151.

[100] L. Heikinheimo, D. Baxter, K. Hack, M. Spiegel, M. Hamalainen, U. Krupp, K. Penttila Y M. Arponen, Mater. Corros. 57 (2006) 230-236. doi:10.1002/maco.200503929

[101] A. Encinas-Oropesa, N.J. Simms, P.J. Kilgallon, S. Turna Y J.E. Oakey, Proc. Eurrocorr 2005, European Federation of Corrosion, Lisboa (Eds), Portugal, 2005.

[102] E.Arias Del Campo, A. Keer-Rendon, L. Manzanares-Papayanopoulos Y R. Bautista- Margulis, Rev. Metal. Madrid Vol. Extr. (2003) 15-22.

Downloads

Published

2006-08-30

How to Cite

Berlanga-Labari, C., & Fernández-Carrasquilla, J. (2006). Review about corrosion of superheaters tubes in biomass plants. Revista De Metalurgia, 42(4), 299–317. https://doi.org/10.3989/revmetalm.2006.v42.i4.29

Issue

Section

Reviews

Most read articles by the same author(s)