High temperature corrosion resistant coatings for gas turbine components
DOI:
https://doi.org/10.3989/revmetalm.2007.v43.i5.82Keywords:
Oxidation, Corrosion, Coating, Power generation, Aeronautic, TurbineAbstract
Hot section gas turbine components are made of superalloys, developed to withstand high temperatures in conditions in which mechanical stresses are high and that require high surface stability. However, during the 50s it became evident that compositions resulting in high mechanical strength for these materials were not compatible with those offering optimal protection from the working environments. The idea of employing protective coatings over materials with high mechanical strength resulted therefore from this situation. Presently, both aeronautic and power generation turbines operate at temperatures within the 900-1400 °C, thanks to these coatings, indispensable for their correct operation. In this work, the principal degradation mechanisms in these operating conditions and the different type of coatings presently employed by the industrial sector are described, beginning by the oldest Ni or Co aluminides, following with the addition of other metals such as Pt, Cr, etc. to the former coatings in order to increase their useful life, continuing with the overlay MCrAlY coatings and finishing with the thermal barrier coating systems. Moreover, the corresponding deposition techniques industrially employed to deposit these coatings are described, and finally, an insight of the latest research lines currently being developed is also included.
Downloads
References
[1] J. Stringer, Surf. Coat. Technol. 108-109 (1998) 1-9. doi:10.1016/S0257-8972(98)00642-2
[2] G.W. Goward, Surf. Coat. Technol. 108-109, (1998) 73-79. doi:10.1016/S0257-8972(98)00667-7
[3] J.L. Smialek y G.H. Meier, Superalloys II, C.T. Sims, N.S. Stoloff y W.C. Hadel (Eds.), John Wiley Sons, 1967, pp. 293-326.
[4] A.S. Khanna, High Temperature. Oxidation and Corrosion., Ed. ASM International, Ohio, USA, 2002, pp. 109-134.
[5] F.S. Pettit y C.S. Giggins, Superalloys II, C.T. Sims, N.S. Stoloff y W.C. Hadel (Eds.), John Wiley Sons, 1967, pp. 327-358.
[6] A.S. Khanna, High Temperature Oxidation. And Corrosion, Ed. ASM International, Ohio, USA, 2002, pp. 172-201.
[7] J.L. Smialek, C.E. Lowell, J. Electrochem. Soc. 121 (1974) 800. doi:10.1149/1.2401922
[8] C. Coddet, Mater. Sci. Forum, 461-464 (2004) 193-464.
[9] J. Stinger E I.G.Wright, Mater. Sci. Forum 369-372 (2001) 1-22.
[10] G.W. Goward y D.H Boone, Oxid. Met. 3 (1973) 475-495. doi:10.1007/BF00604047
[11] P.S: Liu, K.M. Liang, H.Y. Zhou, S.R. Gu, X.F. Sun, H.R. Guan, T. Jin, y K.N. YANG, Surf. Coat. Technol. 175 (2001) 75-79.
[12] G.W. Goward, D.H Boone y C.S. Giggins, Trans. Am. Soc. Met. 60 (1967) 228-241.
[13] C. Houngninou, S. Chevalier y J.P. Larpin, Mater. Sci. Forum 461-464 (2004) 273-280.
[14] J.W. Lee y y.C. Kuo, Surf. Coat. Technol. 201 (2006) 3.867-3.871.
[15] A.B. Smith, A. Kempster y J. Smith, Surf. Coat. Technol. 120-121 (1999) 112-117. doi:10.1016/S0257-8972(99)00346-1
[16] K. L. Choy, Prog. Mater. Sci. 48 (2003) 57-170. doi:10.1016/S0079-6425(01)00009-3
[17] T.A: Kircher, B.G. Mcmordie y A. Mccarter, Surf. Coat. Technol. 68-69 (1994) 32-37. doi:10.1016/0257-8972(94)90134-1
[18] R. Streiff, J.M. N’gandu Muamba y D.H. Boone, Thin Solid Films 73 (1980) 43-52. doi:10.1016/0040-6090(80)90327-2
[19] K. Godlewski y E. Godlewska, Mater. Sci. Eng. 8 (1987) 103-109. doi:10.1016/0025-5416(87)90073-5
[20] R. Bianco, R. Rapp y J.L. Smialek, J. Electrochem. Soc. 140 (1993) 1.191-1.203.
[21] B.M. Warnes, Surf. Coat. Technol. 146-147 (2001) 7-12. doi:10.1016/S0257-8972(01)01363-9
[22] N. Czech, W. Schmitz y W. Stamm, Surf. Coat. Technol. 76-77 (1995) 28-36.
[23] D.K. Gupta y D.S. Duval, US Patent No. 4,585,481 (1986).
[24] H.J. Rätzer-Scheibe, K. Fritscher y W Wirth, High Temperature Alloys for Gas Turbines and Other Applications,W. Bets et al. (eds.), D. Reibel Publishing Co. Dordrecht, 1986, pp. 1.205-1.214.
[25] K. Fritscher, C. Leyens y U. Schulz, Mater. Sci. Forum 369-372 (2001) 703-710.
[26] M. Shibata, S. Kuroda, M. Watanabe y y. Sakamoto, Mater. Sci. Forum 522-523 (2006) 339-344.
[27] B. Wielage, A Wank, H. Phockurska, T. Grund, C. Rupprecht, G. Reisel y E. Friesen, Surf. Coat. Technol. 201 (2006) 2.032- 2.037.
[28] S.J. Grisaffe, NASA TMX-3410 (1976).
[29 ] A.G. Evans, D.R. Mumm, J.W. Hutchinson, G.H. Meier y F.S. Pettit, Prog. Mater. Sci. 46 (2001) 505-553. doi:10.1016/S0079-6425(00)00020-7
[30] A.C. Fox y T.W. Clyne, Surf. Coat. Technol. 184 (2004) 311-321. doi:10.1016/j.surfcoat.2003.10.018
[31] D. Stöver y C. Funke. J. Process. Tech. 92-92 (1999) 195-202.
[32] D. J. Wortman, B.A. Nagaraj y E.C. Duderstadt, Sci. Eng. A A121 (1989) 433-440. doi:10.1016/0921-5093(89)90798-3
[33] J. Toscano, R. Va‚En, A. Gil, M. Subanovic, D. Naumenko, L. Singheiser y W.J. Quadakkers, Surf. Coat. Technol. 201 (2006) 3.906-3.910.
[34] A. Rabiei y A.G. Evans, Acta Materialia 48 (2000) 3.963-3.976.
[35] V.K. Topylgo, D.R. Clarke y K.S. Murphy, Surf. Coat. Technol. 146-147 (2001) 124-131. doi:10.1016/S0257-8972(01)01482-7
[36] C. Coddet, Surf. Coat. Technol. 201 (2006) 1.969-1.974.
[37] K. Landes, Surf. Coat. Technol. 201 (2006) 1.948-1.954.
[38] B. Gleeson, H. Wang, S. Hayashi y D. Sordelet, Mater. Sci. Forum 461-464 (2004) 213.
[39] B.A. Pint, K.L. More y I.G. Wright, High Temp. 20 (2003) 275-386.
[40] G, Sheffknecht, Q. Chen y G. Weissinger, Proc. 6th Int. Charles Parson Turbine Conf. E. Strand et al (Eds.), Londres, 2003, pp. 113-128.
[41] V. Deodeshmukh, N. Mu, B. Li y B. Gleeson, Surf. Coat. Technol. 201 (2006) 3.836-3.840.
[42] T.J. Nijdam, G.H. Marijnissen, E. Vergeldt, A.B. Kloosterman yw.G. Sloof, Oxid. Met. 66 (2006) 269-293. doi:10.1007/s11085-006-9036-8
[43] V.K. Tolpygo, D.R. Clarke, Surf. Coat. Technol. 200 (2005) 1.276–1.281.
[44] D. Monceau, F. Crabos, A. Malié, y B. Pieraggi, Mater. Sci. Forum 369-372 (2001) 607-614.
[45] U. Kaden, C. Leyens, M. Peters y W.A. Kaysser, Elevated Temperature Coatings: Science and Technology, J.M. Hampikian y N.B. Dahotre (Eds.), TMS Warrandale, PA (1999) p. 27.
[46] T. Narita, T. Izumi, T. Nishimoto, y. Shibata, K. Zaini Thisin y S. Hayashi, Mater. Sci. Forum 522-523 (2006) 1-14.
[47] J. A. Haynes, y. Zhang, K.M. Cooley, L. Walker, K.S. Reeves y B.A. Pint, Surf. Coat. Technol. 188-189 (2004) 153-157. doi:10.1016/j.surfcoat.2004.08.066
[48] J.R. Nicholls, K.J. Lawson, A. Johnston y D.S. Rickerby, Mater. Sci. Forum 369-372 (2001) 595-606.
[49] S. Sambasivan y K. Steiner, Patente US6680126-B1 (2004).
[50] J. Glenn, NASA Tech. Briefs, 2005.
[51] K. Bobzin, Erick Lugscheider, N. Bagcivan, High Temp. Mater. Proc. 10 (2006) 103-116. doi:10.1615/HighTempMatProc.v10.i1.80
[52] R. Vassen, M. Dietrich H. Lehmann, X. Cao, G. Pracht, F. Tietz, D. Pitzer y D. Stover, Materliawiss. Werkst. 32 (2001) 673-677.
[53] M.M. Gentleman y D.R. Clarke, Surf. Coat. Technol. 200 (2005) 1.264-1.269.
[54] B.A. Pint, J.A. Haynes, y. Zhang, K.L. More E I.G. Wright, Surf. Coat. Technol. 201 (2006) 3.852-3.856.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2007 Consejo Superior de Investigaciones Científicas (CSIC)
This work is licensed under a Creative Commons Attribution 4.0 International License.
© CSIC. Manuscripts published in both the printed and online versions of this Journal are the property of Consejo Superior de Investigaciones Científicas, and quoting this source is a requirement for any partial or full reproduction.All contents of this electronic edition, except where otherwise noted, are distributed under a “Creative Commons Attribution 4.0 International” (CC BY 4.0) License. You may read here the basic information and the legal text of the license. The indication of the CC BY 4.0 License must be expressly stated in this way when necessary.
Self-archiving in repositories, personal webpages or similar, of any version other than the published by the Editor, is not allowed.