Comparative energy consumption analyses of an ultra high frequency induction heating system for material processing applications

Mehmet Taştan^a, Hayrettin Gökozan^a, Sezai Taşkin^b, Uğur Çavdar^c,*

^aCelal Bayar University, Turgutlu Vocational School, Department of Electric & Energy, 45400 Manisa, Turkey

^bCelal Bayar University, Engineering Faculty, Department of Electrical & Electronics Eng., 45140 Manisa, Turkey

^cCelal Bayar University, Turgutlu Vocational School, Department of Machinery, 45400 Manisa, Turkey

*Corresponding author: ugur.cavdar@cbu.edu.tr

1. INTRODUCTIONTOP

Titanium has emerged as an important metal for a lots of applications. Ti-6Al-4V is one of the most important titanium alloys in the industry applications. This composition is generally using due to its high specific strength, high operating temperature and corrosion resistance (İbrahim et al., 2013).

Ibrahim et al. (2013) reported the effects of the Si-addition as a grain refiner on microstructure and properties of Ti-6Al-4V alloy. Babu and Lindgren (2013) studied dislocation density based model for plastic deformation and globularization of Ti-6Al-4V. Li et al. (2013) used Ti-6Al-4V in their work. Their studies about influence of heat treatment of hot continuous rolled titanium based material. In addition to the Ti-6Al-4V studies, Rhaipu (1998) worked about superplastic forming of same titanium alloy.

In several studies induction systems have been used for heating applications of Ti-6Al-4V. Brunelli et al. (2009) 450 kHz (high frequency), Markovsky and Semiatin (2010); Markovsky and Semiatin (2011) 400 kHz (high frequency) induction systems were used in their studies. In addition to using high frequency for the heat treated of Ti-6Al-4V materials, in this study same titanium composition heat treated by ultra-high frequency (900 kHz) induction system. In many different applications induction heating systems are being used. For example forging (Çavdar, 2014), medium frequency sintering (Çavdar et al., 2014a; Çavdar et al., 2014b; Çavdar et al., 2014c; Çavdar and Atik, 2014), ultra-high frequency welding (Çavdar and Gulşahin, 2014; Çavdar and Kusoğlu, 2014; Çavdar et al., 2014d), ultra-high frequency sintering (Sarı and Çavdar, 2015) and modelling (Riera and Prado, 2006) applications of the iron and/or iron based materials.

Brunelli et al. (2009) investigated the diffusion treatment of Ni-B coatings by using induction heating generator. They were hardened the surface of Ti-6Al-4V alloy via induction. For bulk materials having a complex shape, induction and salt bath, could be used. For example, Semiatin and Sukonnik (1997) used rapid induction heating to form graded microstructures. Titanium alloys were heated by induction and applied by Nishikiori et al. (1996) and Benedetti et al. (2005). In both of these investigations, it was employed for local heating, but the comparatively long exposure times at high temperatures resulted in relatively coarse-grains and hence poor ductility.

Most of the energy generated in the world is consumed by the industry. One of the most significant prerequisites to be able to compete in the generation industry is to decrease the generation costs. The losses in the raw material, interruptions in the generation lines and excessive energy consumption are among the most important factors that affect the cost (Delgado-Gomes et al., 2013).

Power consumption is an important issue that affects all parts of the life. Hence, power consumption should be taken into consideration during the design of home appliances (Tsai et al., 2013), electronic devices (Han et al., 2014), various communication systems (Hinton et al., 2011; Yu et al., 2012), device and machines used in the industry (especially induction motors). To that end, energy efficiency of the devices, which are used in all parts of the life, should be high.

Taskin and Gokozan (2011) made the harmonic analysis using the power parameters of 75 kW induction motor used in industry. Gokozan et al. (2014) made the power quality analysis under different load status of an induction furnace with 350 kVA power and 1 kHz operation frequency used in steel industry. In another study, Ozdemir and Taştan (2014) made the inter-harmonic analysis of the power system using the power data of an arc furnace. In this study; also, energy consumption analysis have been made using the same data collection system (Taskin and Gokozan, 2011; Gokozan et al., 2014; Ozdemir and Taştan, 2014).

Çavdar and Atik (2014) also have made a study covering the energy consumption during the sintering process of iron based powdered metals. Two different sintering processes have been performed within the scope of this study. In a part of the study, sintering process has been made with 12 kW, 50 kHZ induction device and with a medium frequency induction system for the iron based powdered metal materials. In the other part of the study, iron based powdered metal pieces have been sintered using the conventional sintering method which is mostly used in industry. Based on the energy consumed in these two studies, energy consumption per kg has been calculated for each system. Induction sintering process consumes approximately 3.5 times less electrical energy than the conventional process for 1 kg powder compact.

Ultra High Frequency Induction Heat Treatment (UHFIHT) is a rapid heat process. Titanium materials are very important in the automotive, aero-plane, space and biomedical applications. In industrial applications, the most important point is the cost of the application.

In this study, it has been seen that in heating with ultra high frequency induction, the increase in energy consumption is directly linked to the increase in process temperature. Besides, it has been seen that the energy consumption, during the time passed until the samples reach to the desired level, is higher and the energy consumption decreases in the next process.

2. EXPERIMENTAL STUDIESTOP

In this work, two different types of experiment were investigated. One of them is heat treatment of the titanium materials, other one is the heating durations (from 600 °C to 1120 °C) of the titanium materials. For both experiments, a horizontal titanium based materials and a horizontal coil was used for ultra-high frequency induction heat treatment (UHFIHT) application. The diamination’s of the titanium materials are the diameter 16 mm and the height 5 mm. The heat treatment was applied to the samples the coil of the induction system. Diameter of 4 mm and a wall thickness of 0.5 mm of the induction coil was used for heat treatment application. The copper wire was wrapped one making a coil with an inner diameter of 22 mm. Magnetic flux was achieved homogenously due to the centering the titanium materials. Five different bulk materials were used for three different UHFIHT process. The energy costs were the average of the calculations. All bulk materials were heat treated by 2.8 kW, 900 kHz (ultra-high frequency) induction system under atmospheric environment. The temperature of the bulk materials was measured by an infrared thermometer (±5 °C). The heating temperatures were measured and fixed by the infrared laser of the induction system. The chemical composition of Ti-6Al-4V is given in Table 1 as follows.

The numbers are given to the experiments from E1 to E9. The explanations are given in Table 2 and the cycles are given in Fig. 1 and Fig. 2.

2.1. Measurement systemTOP

Measurement system was designed by using the NI LabVIEW program. A multi-functional graphical user interface was designed to save power system data. Using this interface, the changes in the following characteristics of current and voltage signals can be monitored and recorded in the real time: the waveforms of voltage and current in each phase, changes in the power parameters which are apparent, active and reactive power. The overall block diagram of the measurement system is shown in Fig. 1. It consists of voltage and current transducers, data acquisition card and the software. Figure 2 shows the user interface of the measurement system.

The required calculations have been made using the power parameters obtained with data collection system. The formulas in Eq. (1) and Eq. (2) have been used in the calculations.

P=U*I*cosϕ   (1)

were P is the power of the induction heating system (W), U the source voltage (V), I the current drawn by the device (A) and cosϕ the power factor.

were W is the consumed energy amount (Wh), P the power of the induction heating system (W) and t the operating time of the device (s)

On the one hand, three different heat treatment processes were applied to the titanium based samples as given in Fig. 3. The all heat treatments were done at 900 °C for 1 minute and then three different quenching temperatures were applied to the Ti based samples from 600 °C to 700 °C for 30 seconds.

On the other hand, for several heating durations from 600 °C to 1120 °C Ti based materials were heated for half minute. For five different heating durations are illustrated in Fig. 4.

Power and energy consumption values calculated with the formula in Eq. (1) and Eq. (2) are given in Table 3.

3. RESULTS AND DISCUSSIONSTOP

From the data collected during the study, Current-Time graph of the induction heating process under 700 °C is given in Fig. 5; Power-Time graph is given in Fig. 6.

When the Fig. 5 and Fig. 6 is reviewed, it is clearly seen that the power consumption is high in first 7 seconds of heating system (Period-I) and it is lower in the following period of time (Period-II). After the material reaches to the desired temperature level, power consumption decreases. This is similar for all temperature levels as seen in Fig. 7.

The power consumption values of the experiments between E5 and E9 means the temperature durations from 600 °C to 1120 °C are given in Fig. 8. All experiments were applied the samples in 30 seconds after the samples temperatures were grow up to the fixed temperature.

In these experiments which are made under equal process durations and different temperatures, power consumption has increased depending on the temperature. The increase in power consumption is seen in power-temperature graph in Fig. 8, power-time graphs in Fig. 6 and Fig. 7.

Considering the energy consumption values in Eq. (2), energy costs of the processes, energy unit price 0.0861 $/kWh (electrical price was taken from the web page of www.enerjienstitusu.com/elektrik-fiyatlari/) and material weight have been calculated for 2 g. Process costs per material and kg are shown in Table 4.

The total cost of the heat treatment applications is given via bar graph in Fig. 9 as follows.

It is seen on the graph in Fig. 9 that energy costs increase depending on the increase of temperature values in stress relieving processes.

In Fig. 10 energy costs per Kg are seen for the 30 seconds long processes under five different temperatures between 600 °C and 1120 °C.

When the temperature is increased from 600 °C to 900 °C, it is seen that the change in energy consumption is 65.2% while the change in temperature is 50%. When the temperature is increased from 900 °C to 1120 °C, it is seen that the change in energy consumption is 52.77% while the change in temperature is 24.4%. From all these results, it is seen that ratio between the increase in temperature and the cost increase are not same.

In the study of Brunelli et al. (2009), they were used 450 kHz high frequency and 100 kW capacity induction generator. They were obtained by immersion in nickel chloride aqueous solutions with sodium borohydride for electroless nickel-boron coatings on Ti-6Al-4V alloy. The diffusion treatments were carried out by induction heating at 1020 °C in 100 seconds. They were compared the induction heating with conventional method. This obtained previously by heat treatments in oven at 800 °C for 40 hours.

Markovsky and Semiatin used 400 kHz high frequency induction generator and variable power level of 3–5 kW for heating the Ti-6Al-4V rapidly (Markovsky and Semiatin, 2010; Markovsky and Semiatin, 2011). They could be control the heating durations within 0.1 seconds.

In contrast to using the high frequency 400 kHz (Brunelli et al., 2009) or 450 kHz (Markovsky and Semiatin, 2010; Markovsky and Semiatin, 2011) induction systems, in this study 900 kHz ultra-high frequency induction system was used for heating application of the Ti-6Al-4V alloy. Our heating frequency is approximately two times higher than the other studies on the literature. Induction frequency is the directly proportional with penetration depth of the magnetic field.

As a result of the studies, samples reach to the desired temperature level very fast in the heating with induction. So, energy consumption is higher in this period (Period-I). In the following process (Period-II) energy consumption decreases as the temperature is kept stable. In the processes made for different temperatures, it has been seen that the temperature increase rate and energy consumption increase rates are not same.

4. CONCLUSIONSTOP

The conclusions of ultra-high frequency induction heating application of Ti-6Al-4V materials, following results were obtained:

ACKNOWLEDGEMENTTOP

The authors present their special thanks to the Celal Bayar University Scientific Research Projects Commission for supporting this study under project numbers 2012-052 and 2012-022.