Electrochemical noise evaluation of anodized aluminum. Comparative study against corrosion behaviour in the atmosphere
Keywords:Aluminum, Corrosion, Electrochemical noise, Anodized aluminum, Atmospheric corrosion
The present work reports the evaluation of aluminum and anodized aluminum by electrochemical noise, as a part of the PATINA/CYTED project of the working group Nº 5. A visual examination is also made. The samples were exposed at several Ibero-American atmospheres up to 2 years of exposure. Different thickness of anodized aluminum were evaluated. The electrochemical potential noise of the 5 μm unexposed sample (pattern) showed a different behaviour to that showed by the other anodized specimens. This could be due to a slower sealed of the samples of higher thickness. The same behaviour was observed on the samples exposed at the rural station El Pardo. According to the visual examination, the samples of bare aluminum and those of anodized 5 μm thickness were the most affected by pitting corrosion in the highly polluted atmospheres. A good correlation between corrosion behaviour determined by visual examination and EN was obtained.
How to Cite
Copyright (c) 2003 Consejo Superior de Investigaciones Científicas (CSIC)
This work is licensed under a Creative Commons Attribution 4.0 International License.© CSIC. Manuscripts published in both the printed and online versions of this Journal are the property of Consejo Superior de Investigaciones Científicas, and quoting this source is a requirement for any partial or full reproduction.
All contents of this electronic edition, except where otherwise noted, are distributed under a “Creative Commons Attribution 4.0 International” (CC BY 4.0) License. You may read here the basic information and the legal text of the license. The indication of the CC BY 4.0 License must be expressly stated in this way when necessary.
Self-archiving in repositories, personal webpages or similar, of any version other than the published by the Editor, is not allowed.