Influence of Rotational Speed on the Microstructure and Mechanical Response of ECO-AZ31 Magnesium Tubes Processed by Friction Stir Extrusion from Recycled Chips
DOI:
https://doi.org/10.3989/revmetalm.e295.1761Keywords:
ECO-AZ31 alloy, Friction Stir Extrusion (FSE), Mechanical characterization, Microstructural characterization, Recycled chips, TubesAbstract
ECO-AZ31 magnesium alloy modified with 1 wt.% CaO, was investigated for the production of thinwalled tubes by Friction Stir Extrusion (FSE), employing recycled chips through solid-state consolidation. The study focused on the influence of tool rotational speed, ranging from 500 to 1000 rpm, on the consolidation quality, microstructure and mechanical properties of the extruded tubes. The results indicate that low rotational speeds lead to poor material consolidation and surface defects due to insufficient heat generation, whereas high rotational speeds caused overheating and excessive grain growth. In contrast, intermediate rotational speeds were found to be optimal, as they resulted in defect-free tubes with a wall thickness of ~500 μm, exhibiting a refined microstructure (achieving grain sizes in the range of 5–7 μm in the inner region) and improved microhardness (with values close to 80 HV). Microstructural analysis revealed a heterogeneous microstructure throughout the tube wall thickness, associated with the thermal and deformation gradients. At intermediate rotational speeds, {10 1 2} tensile twinning was activated as the dominant mechanism of deformation accommodation, partially reducing dislocation accumulation and softening the texture, leading to a localized decrease in hardness despite the refined grain size. These results demonstrate that the combined effect of heat generation, plastic deformation, dynamic recrystallisation, and twinning determines the final tube properties, confirming FSE as a sustainable and energy-efficient route for producing thin-walled tubes from recycled machining chips.
Downloads
References
Abu-Farha, F. (2012). A preliminary study on the feasibility of friction stir back extrusion. Scr. Mater. 66 (9), 615–618.
Adnan, M., Amantia, S., Puleo, R., Ingarao, G., Fratini, L. (2025). Recycling magnesium alloy AZ31B chips via friction stir consolidation: A sustainable approach, in: Mater. Res. Proc. 54, 2546–2555.
Ahmadkhanbeigi, M., Shapourgan, O., Faraji, G. (2017). Microstructure and mechanical properties of Al tube processed by friction stir tube back extrusion (FSTBE). Trans. Indian Inst. Met. 70, 1849–1856.
Akbari, M., Asadi, P., Abdi Behnagh, R., Bedir, F., Choupani, N., Sadowski, T. (2024). Process parameters and tool design in friction stir extrusion: A sustainable recycling technique. Eng. Rep. 7 (1), e12060.
Amukarimi, S., Mozafari, M. (2022). Biodegradable magnesium biomaterials – Road to the clinic. Bioengineering 9 (3), 107.
Asadi, P., Akbari, M., Talebi, M., Peyghami, M., Sadowski, T., Aliha, M.R.M. (2023). Production of LM28 tubes by mechanical alloying and using friction stir extrusion. Crystals 13 (5), 814.
Barnett, M.R. (2007). Twinning and the ductility of magnesium alloys: Part II. “Contraction” twins. Mater. Sci. Eng. A 464 (1-2), 8–16.
Behnagh, R.A., Shen, N., Ansari, M.A., Narvan, M., Besharati Givi, M.K., Ding, H. (2016). Experimental analysis and microstructure modeling of friction stir extrusion of magnesium chips. J. Manuf. Sci. Eng. 138 (4), 041008.
Buffa, G., Campanella, D., Fratini, L., Micari, F. (2016). AZ31 magnesium alloy recycling through friction stir extrusion process. Int. J. Mater. Form. 9, 613-618.
Buffa, G., Campanella, D., Adnan, M., La Commare, U., Ingarao, G., Fratini, L. (2024). Improving the industrial efficiency of recycling aluminum alloy chips using friction stir extrusion: Thin wires production process. Int. J. of Precis. Eng. and Manuf.-Green Tech. 11, 1133-1146.
Chai, F., Zhang, D., Li, Y. (2014). Effect of thermal history on microstructures and mechanical properties of AZ31 magnesium alloy prepared by friction stir processing. Materials 7 (3), 1573–1589.
Chaudry, U.M., Tariq, H.M.R., Zubair, M., Ansari, N., Jun, T.S. (2023). Implications of twinning on the microstructure development, crystallographic texture and mechanical performance of Mg alloys – a critical review. J. Magn. Alloys 11 (11), 4146–4165.
Chen, L., Zhu, J., Ge, N., Liu, Y., Yan, Z., Liu, G., Li, Y., Wang, Y., Wu, G., Qiu, T., Dia, H., Han, J., Guo, C. (2025). A biodegradable magnesium alloy promotes subperiosteal osteogenesis via interleukin-10- dependent macrophage immunomodulation. Biomaterials 318, 122992.
D’Errico, F., Garcés, G., Hofer, M., Kim, S.K., Pérez, P., Cabeza, S., Adeva, P. (2013). Mechanical properties of AZ31 alloy processed by an eco-sustainable route. Rev. Metal. 49 (6), 405–415.
Friedrich, H.E., Mordike, B.L. (2006). Magnesium Technology. Metallurgy, Design Data, Applications. Springer, Germany.
García Gutiérrez, I., Elduque, D., Pina, C., Tobajas, R., Javierre, C. (2020). Influence of the composition on the environmental impact of a casting magnesium alloy. Sustainability 12 (24), 10494.
Hort, N., Wiese, B., Dieringa, H., Kainer, K.U. (2015). Magnesium melt protection. Mater. Sci. Forum 828–829, 78–81.
Hottle, T., Caffrey, C., McDonald, J., Dodder, R. (2017). Critical factors affecting life cycle assessments of material choice for vehicle mass reduction. Transp. Res. Part D 56, 241–257.
Huang, G.J., Wang, L.Y., Huang, G.S., Pan, F.S. (2005). Dynamic recrystallization and microstructure evolution in AZ31 magnesium alloy during thermomechanical processing. Mater. Sci. Forum. 489–411, 215–218.
Hou, D., Zhu, Y., Li, Q., Liu, T., Wen, H. (2019). Effect of {10–12} twinning on the deformation behavior of AZ31 magnesium alloy. Mater. Sci. Eng. A 746, 314-321.
Jata, K.V., Semiatin, S.L. (2000). Continuous dynamic recrystallization during friction stir welding of high-strength aluminum alloys. Scr. Mater. 43 (8), 743–749.
Keshavarz, Z., Barnett, M.R. (2006). EBSD analysis of deformation modes in Mg–3Al–1Zn. Scr. Mater. 55 (10), 915–918.
Klein, R.W., Williams, B.W., McKinley, J., Einhorn, J.R., Agnew, S.R. (2016). Exploration of thin-walled magnesium alloy tube extrusion for improved crash performance. In: Magnesium Technology 2016, Singh, A., Solanki, K., Manuel, M.V., Neelameggham, N.R. (Eds.), Springer, pp. 223–228.
Kulekci, M.K. (2008). Magnesium and its alloys applications in automotive industry. Int. J. Adv. Manuf. Technol. 39, 851–865.
Lee, K., Jo, H., Kim, S. (2006). Effect of CaO addition on ignition behavior in molten AZ31 and AZ91D magnesium alloys. Rare Met. 25 (6), 155–159.
Li, B.H., Yang, K., Wang, X. (2016). Biodegradable magnesium wire promotes regeneration of compressed sciatic nerves. Neural Regen. Res. 11 (12), 2012–2017.
Liu, X.C., Sun, Y.F., Nagira, T., Ushioda, K., Fujii, H. (2019). Evaluation of dynamic development of grain structure during friction stir welding of pure copper using a quasi in situ method. J. Mater. Sci. Technol. 35 (7), 1412–1421.
Liu, F.C., Feng, A.H., Pei, X., Hovanski, Y., Mishra, R.S., Ma, Z.Y. (2024). Friction stir-based welding, processing, extrusion and additive manufacturing. Prog. Mater. Sci. 1 46, 1 01330.
Lu, J.W., Huang, D., Fan, B.X., Bie, T., Sun, K., Fezzaa, K., Gong, X.L., Luo, S.N. (2016). Anisotropic deformation of extruded magnesium alloy AZ31 under uniaxial compression: A study with simultaneous in situ synchrotron x-ray imaging and diffraction. Acta Mater. 120, 86–94.
Lu, Y., Deshmukh, S., Jones, I., Chiu, Y.L. (2021). Biodegradable magnesium alloys for orthopaedic applications. Biomater. Transl. 2 (3), 214–235.
Mao, T., Yu, T., Cheng, Y., Luo, X., Huang, X., Xin, Y. (2025). Mg–Al–Mn magnesium alloy processability and its extrusion simulation of complex profiles for automotive battery trays. J. Mater. Res. Technol. 39, 513-527.
McNelley, T.R., Swaminathan, S., Su, J.Q. (2008). Recrystallization mechanisms during friction stir welding/processing of aluminum alloys. Scr. Mater. 58 (5), 349–354.
Medina, J., Garces, G., Pérez, P., Adeva, P. (2025). Feasibility of a circular process to manufacture high-performance Mg alloy profiles by extruding recycled chips from machining processes. In: Magnesium Technology. Springer, pp. 125–131.
Meyers, M.A., Mishra, A., Benson, D.J. (2006). Mechanical properties of nanocrystalline materials. Prog. Mater. Sci. 51 (4), 427–556.
Milner, J., Abu-Farha, F. (2014). Microstructural evolution and its relationship to the mechanical properties of Mg AZ31B friction stir back extruded tubes. In: Magnesium Technology 2014. Springer, Cham, 355–360.
Mironov, S., Onuma, T., Sato, Y.S., Kokawa, H. (2015). Microstructure evolution during friction-stir welding of AZ31 magnesium alloy. Acta Mater. 100, 301–312.
Mordike, B.L., Ebert, T. (2001). Magnesium properties-applications-potential. Mater. Sci. Eng. A 302 (1), 37–45.
Nandan, R., Roy, G.G., DebRoy, T. (2006). Numerical simulation of three-dimensional heat transfer and plastic flow during friction stir welding. Metall. Mater. Trans. A 37, 1247–1259.
Puleo, R., Adnan, M., Ingaro, G., Buffa, L., Fratini, L. (2025). Investigating the tube production via friction stir extrusion of aluminum chips. Mater. Res. Proc. 57, 352-359.
Rahimpour Golroudbary, S., Makarava, I., Kraslawski, A. (2022). Environmental assessment of global magnesium production. Miner. Process. Extr. Metall. Rev. 4 4 (6), 389-406.
Rao, K.P., Prasad, Y.V.R.K., Dzwonczyk, J., Hort, N., Kainer, K.U. (2012). Hot deformation mechanisms in AZ31 magnesium alloy extruded at different temperatures: Impact of texture. Metals 2 (3), 292–312.
Saad, M.H., Jarrah, O.M., Nazzal, M.A., Darras, B.M., Kishawy, H.A. (2020). Sustainabilitybased evaluation of Friction Stir Back Extrusion of seamless tubular shapes. J. Clean. Prod. 267, 121972.
Sabour, M.R., Taherkhani, E., Rezaei, A.R., Zohrevand, M., Safahi, H., Faraji, G. (2024). Solid-state recycling of magnesium and its alloys via plastic deformation: An overview of processing and properties. J. Mater. Res. Technol. 31, 3117–3148.
Saqib, M., Kremmer, K., Opitz, J., Schneider, M., Beshchasna, N. (2024). Evaluation of the degradation properties of plasma electrolytically oxidized Mg alloy AZ31 using fluid dynamic accelerated tests for biodegradable implants. J. Funct. Biomater. 15 (12), 366.
Sarkari Khorrami, M., Movahedi, M. (2015). Microstructure evolutions and mechanical properties of tubular aluminum produced by friction stir back extrusion. Mater. Des. 6 5, 74–79.
Shunmugasamy, V.C., Khalid, E., Mansoor, B. (2021). Friction stir extrusion of ultra-thin wall biodegradable magnesium alloy tubes - Microstructure and corrosion response. Mater. Today Commun. 26.
Suhuddin, U.F.H.R., Mironov, S., Sato, Y.S., Kokawa, H., Lee, C.W. (2009). Grain structure evolution during friction-stir welding of AZ31 magnesium alloy. Acta Mater. 57 (18), 5406–5418.
Sun, L., Zeng, Y., Shen, Z., Yue, C., Yang, Y., Gao, J., Zhang, J., Yuan, Q., Cha, L. (2025). Biodegradable metal-based stents: Advances, challenges, and prospects. J. Funct. Biomater. 16 (9), 315.
Talebi, M., Asadi, P., Akbari, M. (2023). Friction stir extrusion and mechanical alloying of LM13 casting ingot to produce LM28 tubes. J. Mater. Res. Technol. 27, 6672-6687.
Tian, P., Liu, X. (2015). Surface modification of biodegradable magnesium and its alloys for biomedical applications. Regener. Biomater. 2 (2), 135–151.
Wang, L., Fang, G., Qian, L., Leeflang, S., Duszczyk, J., Zhou, J. (2014). Forming of magnesium alloy microtubes in the fabrication of biodegradable stents. Prog. Nat. Sci.: Mater. Int. 24 (5), 500–506.
Wang, Z., Hao, X., Qiu, J., Jin, T., Shu, X., Li, X. (2020). Anisotropic yield criterion of rolled AZ31 magnesium alloy via nanoindentation. Appl. Sci. 10 (24), 8997.
Whalen, S., Overman, N., Joshi, V., Varga, T., Graff, D., Lavender, C. (2019). Magnesium alloy ZK60 tubing made by shear assisted processing and extrusion (ShAPE). Mater. Sci. Eng. A 755, 278–288.
Yan, Z., Fang, M., Lian, Z., Zhang, Z., Zhu, J., Zhang, G., Wang, Y. (2019). Research on AZ80 + 0.4 wt.% Ce ultrathin-walled tubes of magnesium alloys: The forming process, microstructure evolution and mechanical properties. Metals 9 (5), 563.
Yang, X., Sun, S., Zhou, Z., Chen, X., Chen, G. (2023). Continuous extrusion forming technology of magnesiu alloy thin-walled tubules. Materials 16 (17), 5803.
Yi, S., Davies, C.H.J., Brokmeier, H.G., Bolmaro, R., Kainer, K.U., Homeyer, J. (2006). Deformation and texture evolution in AZ31 magnesium alloy during uniaxial loading. Acta Mater. 54 (2), 549–562.
Zhang, T., Zesheng, J., Shuyan, W. (2011). Effect of extrusion ratio on mechanical and corrosion properties of AZ31B alloys prepared by a solid recycling process. Mater. Des. 32 (5), 2742–2748.
Zhang, S., Frederick, A., Wang, Y., Eller, M., McGinn, P., Hu, A., Feng, Z. (2019). Microstructure evolution and mechanical property characterization of 6063 aluminum alloy tubes processed with friction stir back extrusion. JOM 71, 4436–4444.
Published
How to Cite
Issue
Section
License
Copyright (c) 2026 Consejo Superior de Investigaciones Científicas (CSIC)
This work is licensed under a Creative Commons Attribution 4.0 International License.
© CSIC. Manuscripts published in both the printed and online versions of this Journal are the property of Consejo Superior de Investigaciones Científicas, and quoting this source is a requirement for any partial or full reproduction.
All contents of this electronic edition, except where otherwise noted, are distributed under a “Creative Commons Attribution 4.0 International” (CC BY 4.0) License. You may read the basic information and the legal text of the license. The indication of the CC BY 4.0 License must be expressly stated in this way when necessary.
Self-archiving in repositories, personal webpages or similar, of any version other than the published by the Editor, is not allowed.
Funding data
Ministerio de Ciencia, Innovación y Universidades
Grant numbers TED2021-129580B-I00