Solvent Extraction of Copper from Sulfate Solutions Using Acorga OPT5510
DOI:
https://doi.org/10.3989/revmetalm.e297.1784Keywords:
Acorga OPT5510, Copper, Hydrometallurgy, Solvent extraction, StrippingAbstract
This study used a solvent extraction technique with AcorgaOPT5510 extractant in kerosene to examine the extraction of copper ions from the actual leach solution produced after leaching malachite ore in sulfuric acid solutions. On the Cu/Fe separation factor and the effectiveness of copper extraction, the impacts of significant parameters, including stirring speed, contact duration, extractant concentration, beginning solution pH, and temperature, were examined. The following values were chosen as the optimal ones: 1:1, 1.5, 12%, 20 °C, 10 min, 10 min, and 500 rpm for maximum Cu2+ extraction from the aqueous-phase, aqueous/organic phase ratio, equilibrium pH of the aqueous phase, extractant concentration, temperature, contact time, settling time, and stirring speed. Under these conditions, 94% of the copper in the leach solution was removed, yielding about 40.09 Cu/Fe separation factor. A McCabe-Thiele plot was revealed, and it was shown that a two-step extraction procedure would yield the best results. Furthermore, employing a sulfuric acid concentration of 4 mol·L-1 for 10 minutes, the loaded organic phase was stripped and recovered 91% copper.
Downloads
References
Agarwal, S., Ferreira, A.E., Santos, S.M.C., Reis, M.T.A., Ismael, M.R.C., Correia, M.J.N., Carvalho, J.M.R. (2010). Separation and recovery of copper from zinc leach liquor by solvent extraction using Acorga M5640. Int. J. Miner. Process. 97 (1–4), 85–91.
Ahn, J., Cho, Y.-C., Kim, J.-Y., Lee, J. (2026). A Solvent Extraction Study of Copper in Methanesulfonic Acid Solution Using LIX-984N-C. J. Sustain. Metall. 12 (1), 742–756.
Ali, Z., Wilkes, N., Raza, N., Omar, M. (2025). Modified Hydrometallurgical Approach for the Beneficiation of Copper from Its Low-Grade Ore. ACS Omega 10 (15), 14826–14834.
Asghari, H., Safarzadeh, M.S., Asghari, G., Moradkham, D. (2009). The effect of impurities on the extraction of copper from sulfate medium using LIX®984N in kerosene. Russ. J. Non-ferrous Metals 50 (2), 89–96.
Attia, R.M. (2022). Extraction of uranium and copper from acid leached solid waste of Alluoga sedimentary rocks, Southwestern Sinai, Egypt. J. Radioanal. Nucl. Chem. 331 (10), 4297–4308.
Azizi, A., Nozhati, R.A., Sillanpää, M. (2020). Solvent Extraction of Copper and Zinc from Sulfate Leach Solution Derived from a Porcelain Stone Tailings Sample with Chemorex CP-150 and D2EHPA. J. Sustain. Metall. 6 (2), 250–258.
Begum, N., Bari, F., Jamaludin, S.B., Hussin, K. (2012). Solvent extraction of copper, nickel and zinc by Cyanex 272. Int. J. Phys. Sci. 7 (22), 2905–2910.
Chepushtanova, T.A., Yessirkegenov, M.I., Nikoloski, A., Merkibayev, Y.S., Altmyshbayeva, A.Z. (2025). Development of an Enhanced Method for Copper Extraction from Sulfuric Acid Solutions. Complex Use of Mineral Resources 334 (3), 99–109.
Danovska, M., Golomeova, M., Karanfilov, D., Zendelska, A. (2013). Treatment of Fe(III) ions from Leaching Solutions with Neutralization and Precipitation. In: 5th Jubilee Balkan Mining Congress. R. Macedonia. pp. 1–8. [Accessed March 2026]. https://eprints.ugd.edu.mk/id/eprint/7969
Demirkıran, N., Tanaydın, M.K. (2021). Recovery of Cu(II) by Acorga M5640 After Leaching of Malachite Ore in Perchloric Acid Solutions. J. Sustain. Metall.7 (2), 495–505.
Deng, J., Wen, S., Yin, Q., Wu, D., Sun, Q. (2017). Leaching of malachite using 5-sulfosalicylic acid. J. Taiwan Inst. Chem. Engrs. 71, 20–27.
Djokić, J., Radovanović, D., Nikolovski, Z., Andjić, Z., Kamberović, Ž. (2021). Influence of Electrolyte Impurities from E-Waste Electrorefining on Copper Extraction Recovery. Metals 11 (9), 1383.
Feizollahi, S., Azizi, A. (2018). Solvent extraction of copper from an industrial sulfate liquor using Chemorex CP-150. J. Min. Environ. 9 (4), 905–916.
Gotfryd, L., Pietek, G. (2013). Contaminants of post-leaching copper solutions and their behavior during extraction with industrial extractants. Physicochem. Probl. Miner. Process. 49 (1), 133–143.
Haider, S.K., Kim, D., Kang, Y.S. (2021). Four-step eco-friendly energy efficient recycling of contaminated Nd2Fe14B sludge and coercivity enhancement by reducing oxygen content. Sci. Rep. 11 (1), 22255.
Hosseinzadeh, M., Azizi, A., Hassanzadeh, A. (2022). Solvent extraction and kinetic studies of copper from a heap leach liquor using CuPRO MEX-3302. Sep. Sci. Technol. 57 (4), 571–588.
Hu, S.Y.B., Wiencek, J.M. (2000). Copper—LIX 84 Extraction Equilibrium. Sep. Sci. Technol. 35 (4), 469–481.
Jiang, F., Yin, S., Zhang, L., Peng, J., Ju, S., Miller, J.D., Wang, X. (2018). Solvent extraction of Cu(II) from sulfate solutions containing Zn(II) and Fe(III) using an interdigital micromixer. Hydrometallurgy 177, 116–122.
Li, X., Rivera-Torrente, M., Deferm, C., Jones, P.T., Binnemans, K. (2025). Shell GTL Fluid G80: A New Synthetic Aliphatic Diluent for Solvent Extraction of Copper. J. Sustain. Metall. 11 (3), 2688–2702.
Maurelia, R., Zamora, P.P., Galleguillos Madrid, F.M., Jiménez-Arévalo, V.M. (2025). Metal-Assisted Deprotonation as a Key Step in Selective Copper Extraction: A Theoretical and Experimental Study. Int. J. Mol. Sci. 26 (24), 11955.
Nozari, I., Azizi, A. (2020). An Investigation into the Extraction Behavior of Copper from Sulfate Leach Liquor Using Acorga M5640 Extractant: Mechanism, Equilibrium, and Thermodynamics. Min. Metall. Explor. 37 (5), 1673–1680.
Ostadi Hesar, A., Mohammad Beygian, A., Keshavarz Alamdari, E., Allahyari, J., Moradi, A. (2025). Investigation of Aldoxime-Ketoxime Solvent Mixtures for Selective Copper Extraction: In-Depth Performance Evaluation Through RSM, Slope Method Mechanism Determination, Ex(%)-pH and McCabe-Thiele Diagrams. Solvent Extr. Ion Exch. 43 (2), 267–293.
Panigrahi, S., Parhi, P.K., Sarangi, K., Nathsarma, K.C. (2009). A study on extraction of copper using LIX 84-I and LIX 622N. Sep. Purif. Technol. 70 (1), 58–62.
Peelman, S., Kooijman, D., Sietsma, J., Yang, Y. (2018). Hydrometallurgical Recovery of Rare Earth Elements from Mine Tailings and WEEE. J. Sustain. Metall. 4 (3), 367–377.
Pradhan, S., Mishra, S. (2015). A review on extraction and separation studies of copper with various commercial extractants. Metall. Res. Technol. 112 (2), 202.
Ruiz, M.C., González, I., Rodriguez, V., Padilla, R. (2021). Solvent Extraction of Copper from Sulfate–Chloride Solutions Using LIX 84-IC and LIX 860-IC. Miner. Process. Extr. Metall. Rev. 42 (1), 1–8.
Rydberg, J. (2004). Solvent Extraction Principles and Practice, Revised and Expanded. CRC Press, Boca Raton.
Seo, S., Lee, G.S., Kim, H.R., Kim, J.-G. (2021). Characterisation of Parameters Influencing the Phase Separation in Copper Solvent Extraction Systems Using Oxime-Type Extractants for the Field Operation. Metals 11 (11), 1785.
Shen, P., Liu, R., Liu, D., Zhang, X., Jia, X., Song, K. (2019). Dissolution kinetics of malachite in ethylene diamine phosphate solutions. Physicochem. Probl. Miner. Process. 55 (4), 1039–1048.
Sombhatla, S.S., Kumar, A., Mashruwala, S., Rokkam, K.K., Shukla, A. (2016). Comparative study of organic solvents for extraction of copper from ammoniacal carbonate solution. Hydrometallurgy 166, 94–97.
Song, S., Rao, F., Zhang, X. (2011). Effect of morphology on sulphuric acid leaching of malachite ores. Miner. Process. Extr. Metall. Trans. Inst. Min. Metall. 120 (2), 85–89.
Tanaydın, M.K., Demirkıran, N. (2020). Kinetic models for the extraction of copper by Acorga M5640 after leaching of malachite ore in perchloric acid solutions and the stripping of copper from loaded organic phase. Braz. J. Chem. Eng. 37 (2), 399–414.
Tanda, B.C., Oraby, E.A., Eksteen, J.J. (2017). Recovery of copper from alkaline glycine leach solution using solvent extraction. Sep. Purif. Technol. 187, 389–396.
Tinkler, O., Shiels, D., Soderstrom, M. (2009). The ACORGA® OPT series: comparative studies against aldoxime: ketoxime reagents. In: Hydrometallurgy Conference. Johannesburg: The Southern African Institute of Mining and Metallurgy. [Accessed 21 February 2026]. https://www.saimm.co.za/Conferences/Hydro2009/273-282_Tinkler.pdf
Vance, S.S.M., Chatzisymeon, E., Morrison, C.A., Love, J.B. (2025). Recovering copper from e-waste: recyclable precipitation versus solvent extraction with carbon emission assessment. Green Chem. 27 (14), 3789–3804.
Vasilyev, F., Virolainen, S., Sainio, T. (2017). Modeling the phase equilibrium in liquid–liquid extraction of copper over a wide range of copper and hydroxyoxime extractant concentrations. Chem. Eng. Sci. 171, 88–99.
Wang, L., Li, Q., Sun, X., Wang, L. (2019). Separation and recovery of copper from waste printed circuit boards leach solution using solvent extraction with Acorga M5640 as extractant. Sep. Sci. Technol. 54 (8), 1302–1311.
Published
How to Cite
Issue
Section
License
Copyright (c) 2026 Consejo Superior de Investigaciones Científicas (CSIC)
This work is licensed under a Creative Commons Attribution 4.0 International License.
© CSIC. Manuscripts published in both the printed and online versions of this Journal are the property of Consejo Superior de Investigaciones Científicas, and quoting this source is a requirement for any partial or full reproduction.
All contents of this electronic edition, except where otherwise noted, are distributed under a “Creative Commons Attribution 4.0 International” (CC BY 4.0) License. You may read the basic information and the legal text of the license. The indication of the CC BY 4.0 License must be expressly stated in this way when necessary.
Self-archiving in repositories, personal webpages or similar, of any version other than the published by the Editor, is not allowed.