Effect of the addition of 10% (volume fraction) of chromium on the mechanical properties of NiAICr
DOI:
https://doi.org/10.3989/revmetalm.2005.v41.i4.216Keywords:
Ni3Al, microstructure, mechanical properties, powder metallurgy.Abstract
The mechanical properties of Ni3Al-Cr reinforced with 10% in volume fraction of chromium particles produced by powder metallurgy have been studied. For this purpose, milled powders with composition of Ni-20.9Al-8Cr-0.49B (% at.) with and without the addition of 10% in volume fraction of chromium particles have been produced. Both alloys were consolidated by hot isostatic pressing (HIP). After HIP, heat treatment was applied to homogenize the microstructure. The chromium reinforcement has an important effect in the yield strength and ultimate strength increase. The reinforced alloy presents a yield strength of 1300 MPa at room temperature with respect to 800 MPa for the un-reinforced material. After heat treatment, the yield strength of both alloys does not change significantly. However, a decrease in ductility and ultimate tensile strength have been observed
Downloads
Download data is not yet available.
Downloads
Published
2005-08-30
How to Cite
García-Barriocanal, J., Garces, G., Pérez, R., & Adeva, P. (2005). Effect of the addition of 10% (volume fraction) of chromium on the mechanical properties of NiAICr. Revista De Metalurgia, 41(4), 286–291. https://doi.org/10.3989/revmetalm.2005.v41.i4.216
Issue
Section
Articles
License
Copyright (c) 2005 Consejo Superior de Investigaciones Científicas (CSIC)

This work is licensed under a Creative Commons Attribution 4.0 International License.
© CSIC. Manuscripts published in both the printed and online versions of this Journal are the property of Consejo Superior de Investigaciones Científicas, and quoting this source is a requirement for any partial or full reproduction.All contents of this electronic edition, except where otherwise noted, are distributed under a “Creative Commons Attribution 4.0 International” (CC BY 4.0) License. You may read here the basic information and the legal text of the license. The indication of the CC BY 4.0 License must be expressly stated in this way when necessary.
Self-archiving in repositories, personal webpages or similar, of any version other than the published by the Editor, is not allowed.