Surface texture effect on tribologic behaviour in nitrocarburized X40CrMoV5 1 steel layers

Authors

  • V. Miguel Ciencia e Ingeniería de Materiales. Instituto de Desarrollo Regional. Universidad de Castilla-La Mancha
  • A. Calatayud Ciencia e Ingeniería de Materiales. Instituto de Desarrollo Regional. Universidad de Castilla-La Mancha
  • J. Coello Ciencia e Ingeniería de Materiales. Instituto de Desarrollo Regional. Universidad de Castilla-La Mancha
  • A. Martínez Ciencia e Ingeniería de Materiales. Instituto de Desarrollo Regional. Universidad de Castilla-La Mancha
  • A. Caminero Ciencia e Ingeniería de Materiales. Instituto de Desarrollo Regional. Universidad de Castilla-La Mancha

DOI:

https://doi.org/10.3989/revmetalm.2005.v41.iExtra.934

Keywords:

Nitrocarburizing, Friction, Wear, X40CrMoV5 1 steel, Surface roughness

Abstract


In this work the surface roughness behaviour in the forming of gaseous nitrocarburized layers has been analyzed. Ra values from 0.02 to 1.50 μm. has been considered. Obtained results prove a minor influence on layer thickness. A little increase of Ra has been observed. The abrasive wear resistance of nitrocarburized specimens was researched. The carbonitride ε is the only constituent in the about 6 μm thickness layers that have been carried out in this work. The tests revealed a minor wear resistance of the external part in the layers. This way, the external zone is less effective to wear phenomena than the internal. The specimens with small roughness parameters values show a higher poor wear resistance zone.

Downloads

Download data is not yet available.

Downloads

Published

2005-12-17

How to Cite

Miguel, V., Calatayud, A., Coello, J., Martínez, A., & Caminero, A. (2005). Surface texture effect on tribologic behaviour in nitrocarburized X40CrMoV5 1 steel layers. Revista De Metalurgia, 41(Extra), 17–22. https://doi.org/10.3989/revmetalm.2005.v41.iExtra.934

Issue

Section

Articles

Most read articles by the same author(s)

1 2 > >>