Análisis mecánico y microestructural en soldadura de fundición dúctil, mediante procedimiento TIG, con diferentes materiales de aporte y enfriamiento al aire

Jorge  Martínez Alcón; Manuel  Pascual Guillamón; Lorenzo  Solano García; Fidel  Salas Vicente

doi:10.3989/revmetalm.194

Autores/as

Jorge Martínez Alcón PhD student at the Department of Mechanical and Materials Engineering, Polytechnic University of Valencia https://orcid.org/0000-0001-6139-5059
Manuel Pascual Guillamón Institute of Materials Technology, Polytechnic University of Valencia https://orcid.org/0000-0003-0216-5119
Lorenzo Solano García Department of Mechanical and Materials Engineering, Polytechnic University of Valencia https://orcid.org/0000-0003-0535-314X
Fidel Salas Vicente Institute of Materials Technology, Polytechnic University of Valencia https://orcid.org/0000-0003-0834-4425

DOI:

https://doi.org/10.3989/revmetalm.194

Palabras clave:

Fundición dúctil nodular, Metal-base-interfase-metal de soldadura, Reparación, Soldabilidad, TIG

Resumen

En el presente trabajo se analizan las variaciones resistentes y microestructurales de la fundición dúctil soldada mediante la técnica tungsten inert gas (TIG), sin tratamientos térmicos y utilizando diferentes materiales de aporte (fundición maleable perlítica, aleación Fe-Ni y aleación de bronce y manganeso). A partir de cada cupón soldado de dimensiones 100x100x6 mm, se obtienen las probetas para los ensayos mecánicos y microestructurales. Con el análisis cualitativo de las micrografías y el análisis cuantitativo de los resultados de los ensayos mecánicos, que han sido realizados en zonas bien diferenciadas de las uniones soldadas (metal base, interfase y cordón de soldadura), se concluye la idoneidad de este tipo de soldaduras y de la introducción nuevas variables como los tratamientos térmicos previos y/o posteriores a la soldadura. Se han correlacionando las características mecánicas y resistentes con las microestructuras obtenidas en las placas (probetas) para poder evaluar sus ventajas e inconvenientes, así como elaborar conclusiones.

Descargas

Los datos de descargas todavía no están disponibles.

Citas

Abboud, J.H. (2012). Microstructure and erosion characteristic of nodular cast iron surface modified by tungsten inert gas. Mater. Design 35, 677-684. https://doi.org/10.1016/j.matdes.2011.09.029

Askari-Paykani, M., Shayan, M., Shamanian, M. (2014). Weldability of ferritic ductile cast iron using full factorial design of experiment. J. Iron Steel Res. Int. 21 (2), 252-263. https://doi.org/10.1016/S1006-706X(14)60039-X

Bhatnagar, R.K., Gupta, G. (2016). A Review on Weldability of Cast Iron. IJSER 7 (5), 126-131.

Bhatti, A.A., Barsoum, Z., Murakawa, H., Barsoum, I. (2015). Influence of thermo-mechanical material properties of different steel grades on welding residual stresses and angular distortion. Mater. Design 65, 878-889. https://doi.org/10.1016/j.matdes.2014.10.019

Cárcel-Carrasco, F.J., Pérez-Puig, M.A., Pascual-Guillamón, M., Pascual-Martínez, R. (2016). An analysis of the weldability of ductile cast iron using inconel 625 for the root weld and electrodes coated in 97.6% nickel for the filler welds. Metals 6 (11), 283. https://doi.org/10.3390/met6110283

Cárcel-Carrasco, J., Pascual, M., Pérez-Puig, M., Segovia, F. (2017). Comparative study of TIG and SMAW root welding passes on ductile iron cast weldability. Metalurgija 56 (1-2), 91-93.

Chamim, M., Triyono, Diharjo, K. (2017). Effect of electrode and weld current on the physical and mechanical properties of cast iron welding. AIP Conf. Proc. 1788 (1), 030031. https://doi.org/10.1063/1.4968284

De La Torre, U., Loizaga, A., Lacaze, J., Sertucha, J. (2014). As cast high silicon ductile irons with optimised mechanical properties and remarkable fatigue properties. Mater. Sci. Tech. 30 (12), 1425-1431. https://doi.org/10.1179/1743284713Y.0000000483

Ebrahimnia, M., Ghaini, F.M., Gholizade, S., Salari, M. (2012). Effect of cooling rate and powder characteristics on the soundness of heat affected zone in powder welding of ductile cast iron. Mater. Design 33, 551-556. https://doi.org/10.1016/j.matdes.2011.04.063

El-Banna, E.M. (1999). Effect of preheat on welding of ductile cast iron. Mater. Lett. 41 (1), 20-26. https://doi.org/10.1016/S0167-577X(99)00098-1

Gouveia, R.M., Silva, F.J.G., Paiva, O.C., de Fátima Andrade, M., Pereira, L.A., Moselli, P.C., Papis, K.J.M. (2018). Comparing the structure and mechanical properties of welds on ductile cast iron (700 MPa) under different heat treatment conditions. Metals 8 (1), 72. https://doi.org/10.3390/met8010072

Kumar, R., Kumar, M., Trivedi, V., Bhatnagar, R. (2017). Evaluation of Mechanical and Microstructural Properties of Cast Iron with Effect of Pre Heat and Post Weld Heat Treatment. Int. J. Mech. Eng. 4 (5), 1-6. https://doi.org/10.14445/23488360/IJME-V4I5P101

Marques, E.S.V., Silva, F.J.G., Paiva, O.C., Pereira, A.B. (2019). Improving the mechanical strength of ductile cast iron welded joints using different heat treatments. Materials 12 (14), 2263. https://doi.org/10.3390/ma12142263

Merchant Samir, Y. (2015). A Review of Effect of Welding and Post Weld Heat Treatment on Microstructure and Mechanical Properties of Grade 91 Steel. IJRET 4 (3), 574-580. https://doi.org/10.15623/ijret.2015.0403096

Pascual, M., Ferrer, C., Rayón, E. (2009). Weldability of spheroidal graphite ductile cast iron using Ni / Ni-Fe electrodes. Rev. Metal. 45 (5), 334-338. https://doi.org/10.3989/revmetalm.0814

Sellamuthu, P., Samuel, D.G.H., Dinakaran, D., Premkumar, V.P., Li, Z., Seetharaman, S. (2018). Austempered ductile iron (ADI): Influence of austempering temperature on microstructure, mechanical and wear properties and energy consumption. Metals 8 (1), 53. https://doi.org/10.3390/met8010053

Suárez-Sanabria, A., Fernández-Carrasquilla, J. (2006). Microestructura y propiedades mecánicas de una fundición esferoidal ferrítica en bruto de colada para su uso en piezas de grandes dimensiones. Rev. Metal. 42 (1), 18-31. https://doi.org/10.3989/revmetalm.2006.v42.i1.3

UNE-EN 876 (1996). Ensayos destructivos de uniones soldadas en materiales metálicos. Ensayos de tracción longitudinal sobre el metal de aportación en uniones soldadas por fusión. Normalización Española.

UNE-EN 10002-1 (2002). Materiales metálicos: Ensayos de tracción. Parte 1, Método de ensayo a temperatura ambiente. Asociación Española de Normalización y Certificación.

UNE-EN 1563 (2019). Fundición. Fundición de grafito esferoidal. Normalización Española y Certificación.

Wube Dametew, A. (2015). Experimental investigation on weld ability of cast iron. Science Discovery 3 (6), 71-75. https://doi.org/10.11648/j.sd.20150306.15